aluminum sheet 5A06 for ship, automobile and mould
Contact name :
Mingtai AL. industry
5A06 aluminum plate thickness: 1-600mm, widely used in welding structures, cold die forging parts, welding and pulling container stress parts; maritime uses such as ships, and cars, subway light rail, pressure vessels that require strict fire protection (such as liquid tank trucks, refrigerated trucks) , Refrigerated containers), refrigeration devices, TV towers, drilling equipment, transportation equipment. It can also be used in the field of construction, sheet metal parts for oil pipes, transportation vehicles, ships, instruments, street lamp brackets and rivets, hardware products, electrical appliances shells, etc.
1. It is a high-magnesium alloy, which has good strength, good corrosion resistance and machinability in non-heat treatable alloys. The surface is beautiful after anodizing. The arc welding performance is good. The main alloying element in 5A06 alloy is magnesium, which has good corrosion resistance and weldability, as well as medium strength.
3. Excellent corrosion resistance makes 5A06 alloy widely used in maritime applications such as ships, as well as automobiles, aircraft welding parts, subway light rail, pressure vessels (such as liquid tank trucks, refrigerated trucks, refrigerated containers), refrigeration devices, TVs that require strict fire protection Towers, drilling equipment, transportation equipment, missile parts, armor, etc.
3, 5A06 belongs to Al-Mg series alloys, and has a wide range of applications, especially the construction industry is inseparable from this alloy and is a promising alloy. Good corrosion resistance, excellent weldability, good cold workability, and moderate strength.
The corrosion resistance of 5A05 and 5B05 alloys is closely related to the distribution of the second phase (β-Al3Mg2). If the second phase is continuously distributed at the grain boundaries, the alloy will be sensitive to grain boundary corrosion and stress corrosion cracking. Adopting proper annealing system to make β phase get uniform and discontinuous distribution, the corrosion resistance of the alloy is significantly improved.
Cold work hardening, long-term heating during use will reduce the corrosion resistance of the alloy, and even cause spalling corrosion. 5A03 is a two-phase alloy, but the precipitation of β phase along the grain boundary is not continuous, so it has good corrosion resistance.